性能 |
检测
方法 |
单位 |
100%PTFE |
15%
玻纤 |
25%
玻纤 |
15% 石墨 |
25% 碳 |
25%
碳石墨化合物 |
60% 青铜
2% 碳 |
|
模压制品 |
|
表观密度 |
ASTM D792 |
g/cm3 |
2.14-2.18 |
2.19-2.22 |
2.23-2.25 |
2.10-2.15 |
2.05-2.11 |
2.05-2.11 |
3.80-3.90 |
|
线性热膨胀系数 |
ASTM D696 |
1/℃ 10-5 |
12-13 |
11-13 |
7.5-11 |
12-13 |
12-13 |
10-12 |
8-9 |
|
邵氏硬度 |
ASTM D2240 |
points |
≥58 |
60-65 |
62-67 |
55-60 |
60-65 |
62-67 |
65-70 |
|
抗拉强度 |
ASTM D4894
ASTM D4745 |
N/mm2 |
≥24 |
17-24 |
14-21 |
15-20 |
15-20 |
14-18 |
17-23 |
|
断裂伸长率 |
ASTM D4894
ASTM D4745 |
% |
≥250 |
250-300 |
230-270 |
170-250 |
150-200 |
70-120 |
100-160 |
|
抗压强度
1%变形 |
ASTM D695 |
N/mm2 |
4-5 |
6-7 |
8-9 |
6.5-7.5 |
7-9 |
7-9 |
10-11 |
|
受力变形
(24h 13.7N/mm2 23℃) |
ASTM D621 |
% |
14-17 |
10-14 |
7-10 |
8-10.5 |
4.5-6.5 |
5-6 |
5-6 |
|
永久变形
(as above, after 24-h relaxation) |
ASTM D621 |
% |
7-9 |
6-7 |
4-6.5 |
4-6 |
2.5-4 |
2.5-4 |
1.5-2.5 |
|
摩擦系数 |
ASTM D1894 |
/ |
0.06 |
0.12 |
0.13 |
0.07 |
0.13 |
0.11 |
0.13 |
|
磨损因数
PV 100 |
ASTM D3702 |
Cm3*min*10-8
kg*m*h |
2900 |
10-20 |
10-15 |
60 |
20-30 |
16-20 |
10 |
|
挤出制品 |
|
表观密度 |
ASTM D792 |
g/cm3 |
2.14-2.18 |
2.18-2.21 |
2.22-2.24 |
2.09-2.14 |
2.04-2.10 |
3.04-2.10 |
3.80-3.88 |
|
硬度 |
ASTM D2240 |
points |
51-60 |
60-65 |
62-67 |
55-60 |
60-65 |
62-67 |
65-70 |
|
抗拉强度 |
ASTM D4894 |
N/mm2 |
≥20 |
≥15 |
≥13 |
≥14 |
≥14 |
≥12 |
≥13 |
|
断裂伸长率 |
ASTM D4745 |
% |
≥200 |
≥200 |
≥180 |
≥70 |
≥100 |
≥50 |
≥80 |
填充制品为了改善聚四氟乙烯的蠕变特性和耐磨耗性能，以石墨、炭黑、二硫化钼、玻璃纤维、碳纤维、聚苯硫醚等为主要材料对聚四氟乙烯进行填充改造。
主要用途：
垫片、阀座、密封、轴承、滑块、活塞环等。 |